CPVC Pipe Physical Properties
GENERAL Value Test Method
Cell Classification 23447 ASTM D1784
Maximum Service Temp. 200°F  
Color Medium Gray  
Specific Gravity, (g/cu.cm @ 73°F) 1.53 ± 0.02 ASTM D792
Water Absorption % increase 24 hrs @ 25°C 0.03 ASTM D570
Hardness, Rockwell 117 ASTM D785
Poisson's Ratio @ 73°F 0.386  
Hazen-Williams Factor C =150  
Tensile Strength, psi @ 73°F 7,600 ASTM D638
Tensile Modulus of Elasticity, psi @ 73°F 370,000 ASTM D638
Flexural Strength, psi @ 73°F 12,500 ASTM D790
Flexural Modulus, psi @ 73°F 360,000 ASTM D790
Compressive Strength, psi @ 73°F 10,000 ASTM D695
Compressive Modulus, psi @ 73°F 196,000 ASTM D695
Izod Impact, notched, ft-lb/in @ 73°F 2.6 ASTM D256
Coefficient of Linear Expansion (in/in/°F) 3.9 x 10-5 ASTM D696
Coefficient of Thermal Conductivity
3.27 x 10-4
Heat Deflection Temperature Under Load (264psi, Annealed) 228°F ASTM D648
Dielectric Strength, volts/mil 1,250 ASTM D149
Dielectric Constant, 60Hz, 30°F 3.70 ASTM D150
Volume Resistivity, ohm/cm @ 73°F 3.4 x 1015 ASTM D257
Power Factor, 1000Hz 0.007% ASTM D150
GF Harvel CPVC Pipe is non-electrolytic
Flammability Rating V-0, 5VB, 5VA UL-94
Flame Spread Index <10  
Flame Spread <25 ASTM E-84/UL 723
  <25 ULC
Smoke Generation ≤50 ASTM E-84/UL 723
  <50 ULC
Flash Ignition Temp. 900°F  
Average Time of Burning (sec.) <5 ASTM D635
Average Extent of Burning (mm) <10  
Burning Rate (in/min) Self Extinguishing
Softening Starts (approx.) 295°F  
Material Becomes Viscous 395°F  
Material Carbonizes 450°F  
Limiting Oxygen Index (LOI) 60 ASTM D2863
Clean Room Materials Flammability Test FPI= 1.20   SDI= 0.09 FM 4910
Note: The physical properties shown are considered general CPVC physical properties. GF Harvel utilizes several CPVC compounds for the production different CPVC product lines. Different CPVC compounds may exhibit slight variations in actual physicals properties as compared to those stated. Contact GF Harvel Tech Services for additional information if necessary.